Mazkur maqolada JM-380 markali polipropilenning termooksodestruksiya jarayoniga turli omillar — harorat, vaqt, oksidlovchi muhit, aralashtirish tezligi va stabilizatorlar ishtirokining ta’siri kompleks o‘rganilgan. Natijada JM-380 markali polipropilenni termooksidlovchi destruksiyalash uchun quyidagi sharoitlar optimal deb baholandi: harorat – 300 ± 10°C, ishlov vaqti – 30–40 daqiqa, muhit – kislorodli atmosfera (≥15%). Ushbu parametrlar asosida amalga oshirilgan destruksiya jarayonida molekulyar og‘irlik ~60% ga kamayadi, disperslik indeksi 1,8–2,2 oralig‘ida bo‘ladi va funksional guruhlarning paydo bo‘lishi IQ spektroskopik tahlillar orqali isbotlandi. Natijada, polimer-bitum kompozitsiyasi yuqori darajada gomogen, elastik va reologik jihatdan barqaror bo‘ladi.

  • Read count 19
  • Date of publication 28-09-2025
  • Main LanguageO'zbek
  • Pages177-182
Ўзбек

Mazkur maqolada JM-380 markali polipropilenning termooksodestruksiya jarayoniga turli omillar — harorat, vaqt, oksidlovchi muhit, aralashtirish tezligi va stabilizatorlar ishtirokining ta’siri kompleks o‘rganilgan. Natijada JM-380 markali polipropilenni termooksidlovchi destruksiyalash uchun quyidagi sharoitlar optimal deb baholandi: harorat – 300 ± 10°C, ishlov vaqti – 30–40 daqiqa, muhit – kislorodli atmosfera (≥15%). Ushbu parametrlar asosida amalga oshirilgan destruksiya jarayonida molekulyar og‘irlik ~60% ga kamayadi, disperslik indeksi 1,8–2,2 oralig‘ida bo‘ladi va funksional guruhlarning paydo bo‘lishi IQ spektroskopik tahlillar orqali isbotlandi. Natijada, polimer-bitum kompozitsiyasi yuqori darajada gomogen, elastik va reologik jihatdan barqaror bo‘ladi.

Русский

В данной статье комплексно изучено влияние различных факторов - температуры, времени, окислительной среды, скорости перемешивания и стабилизаторов - на процесс термооксидеструкции полипропилена марки JM-380. В результате, для термоокислительной деструкции полипропилена марки JM-380 были оценены следующие оптимальные условия: температура - 300 ± 10°C, время обработки - 30-40 минут, среда - кислородная атмосфера (≥15%). В процессе деструкции, осуществляемой на основе этих параметров, молекулярная масса уменьшается на ~60%, индекс дисперсности находится в пределах 1,8-2,2, а появление функциональных групп доказано ИК-спектроскопическим анализом. В результате полимер - битумная композиция становится высоко гомогенной, эластичной и реологически стабильной.

English

In this article, the influence of various factors - temperature, time, oxidizing medium, mixing speed, and the participation of stabilizers - on the thermooxodestruction process of JM-380 polypropylene was comprehensively studied. As a result, the following conditions were considered optimal for thermo-oxidative destruction of JM-380 polypropylene: temperature - 300 ± 10°C, processing time - 30-40 minutes, medium - oxygen atmosphere (≥15%). In the process of destruction carried out on the basis of these parameters, the molecular weight decreases by ~60%, the dispersity index is in the range of 1.8-2.2, and the appearance of functional groups is proven by IR spectroscopic analysis. As a result, the polymer-bitumen composition is highly homogeneous, elastic, and rheologically stable.

№ Author name position Name of organisation
1 Babajanov J.E. Katta o‘qituvchi Berdaq nomidagi Qoraqalpoq davlat universiteti
2 Mavlonov S. . dotsent Buxoro davlat texnika universiteti
3 Hayitov R.R. Texnika fanlari doktori (DSc) Buxoro davlat texnika universiteti
№ Name of reference
1 Shi Chen Guang // Evaluation of Self-healing Rate of Polymer Modified Asphalt Based on Surface Free Energy// World Transport Convention — 2018/ Highway Engineering/ Beijin, June 2018, p. 179.
2 A. Tabaković, E. Schlangen// Self-Healing Technology for Asphalt Pavements / Self-Healing, Advances in Polymer Science 273, Springer/ 2015.
3 S. O. Ilyin, M. P. Arinina, Yu. S. Mamulat, A. Y. Malkin, V. G. Kulichikhin // Rheological properties of road bitumens modified with polymer and solid nanosized additives// July 2014 Colloid Journal 76(4):425–426.
4 Козлов Г. В., Яновский Ю. Г., Липатов Ю. С. Фрактальный анализ структуры и свойств межфазных слоев в дисперсно-наполненных полимерных композитах // Механика композиционных материалов и конструкций. — 2002. — 8, № 1. — С. 111–112.
5 Коренькова С.Ф., Давиденко О.В. Роль органоминеральных комплексов в структуре битумокомпозиционных вяжущих // Строительные материалы. - 1998. - №11.
6 CHEN, J.S. and C.H. LIN, 1999. Construction of Test Road to Evaluate Engineering Properties of Polymer-Modified Asphalt Binders. International Journal of Pavement Engineering, 01 Feb 2007.
Waiting