497

The results of the study of optical absorption of metal films YBa2
Cu3O6+x  when passing 
through the film direct current to 100 mA are presented. Analysis of the data indicates that the 
relationship between absorption and current arises due to the possibility of filling the localization 
areas with carriers in the current mode (or vice versa, due to the emission of localized carriers to 
the mobility level). Fdor films with substantially nonlinear voltammper characteristic, a strong 
effect  of  current  on  the  value  of  interzone  absorption  was  found.  It  has  been  experimentally 
established that the EO-effect occurs at interzone transitions only in the mode of nonlinear VAC, 
the  amplitude  of  the  effect  increases  with  the  growth  of  current  (voltage),  but  with  the 
linearization of VAC EO-effect disappears. In the field of optical transitions at local levels, this 
effect was not observed. The analysis of results from the point of view of carrier localization and 
delocalization processes.

  • Internet havola
  • DOI
  • UzSCI tizimida yaratilgan sana 23-01-2020
  • O'qishlar soni 459
  • Nashr sanasi 12-12-2019
  • Asosiy tilIngliz
  • Sahifalar28-32
Ўзбек

Bu    maqolada YBa2Cu3O6+x metall    plyonkalari    orqali 100 mA gacha doimiy tok o'tganda 
optik  yutilishlarni  tekshirishning  natijalari  berilgan.Olingan  natijalarning  tahlili  shundan 
iboratki  ,  tok  va  yutilish  orasidagi  bog’lanish  tokli  rejimda  lokalizaciya  sohasining   zaryad 
tashuvchilar  bilan  to'lishi  natijasida  (yoki  teskarisi,  lokal  zaryad  tashuvchilarning 
o'tkazuvchanlik sohasiga o'tgandan keyin) hosil bo'ladi.Nochiziqli vol’tamper harakteristikaga 
ega  bo'lgan  plyonkalar  uchun  zonalararo  yutilish  qiymatiga  tokning  kuchli  ta'siri 
aniqlandi.Eksperiment  yo'li  bilan  aniqlanishicha,  elektr  optik  effekt  faqat  nochiziqli  VAX 
Aerospace engineering
29
rejimida  zonalararo  o'tishda,  tok(kuchlanish)ning  ortishi  natijasida   amplituda  effektining 
o'sishida  hosil  bo'larkan   va  chiziqli  VAX  lar  bo'yicha  elektr  optik  effekt  yo'qolar  ekan.Optik 
o'tishlarning  lokal   sohalarida  bu  effekt  kuzatilmas  ekan.  Zaryad  tashuvchilarning  lokal  va 
delokal  jarayonlari nuqtai  nazaridan qaralib  natijalar  tahlili o'tkazilgan.

Kalit so'z
English

The results of the study of optical absorption of metal films YBa2
Cu3O6+x  when passing 
through the film direct current to 100 mA are presented. Analysis of the data indicates that the 
relationship between absorption and current arises due to the possibility of filling the localization 
areas with carriers in the current mode (or vice versa, due to the emission of localized carriers to 
the mobility level). Fdor films with substantially nonlinear voltammper characteristic, a strong 
effect  of  current  on  the  value  of  interzone  absorption  was  found.  It  has  been  experimentally 
established that the EO-effect occurs at interzone transitions only in the mode of nonlinear VAC, 
the  amplitude  of  the  effect  increases  with  the  growth  of  current  (voltage),  but  with  the 
linearization of VAC EO-effect disappears. In the field of optical transitions at local levels, this 
effect was not observed. The analysis of results from the point of view of carrier localization and 
delocalization processes.

Русский

Представлены  результаты  исследования  оптического  поглощения  металлических 
пленок  YBa
2
Cu3O6+x 
при  пропускании  через  пленку  постоянного  тока  до  100  mA.Анализ 
данных  свидетельствует  о  том,  что  взаимосвязь  поглощения  и  тока  возникает  из-за 
возможности  заполнения  носителями  в  токовом  режиме  областей  локализации(или 
наоборот, из-за выброса локализованных носителей на уровень подвижности). Для пленок 
с существенно нелинейной вольтамперной характеристикой обнаружено сильное влияние 
тока  на  величину  межзонного  поглощения.  Экспериментально  было  установлено,  что 
ЭО-эффект  возникает  на  межзонных  переходах  только  в  режиме  нелинейной  ВАХ, 
амплитуда  эффекта  увеличивается  с  ростом  тока  (напряжения),  но  по  мере 
линеаризации ВАХ ЭО-эффект исчезает. В области оптических переходов на локальных 
уровнях  данный  эффект  не  наблюдался.  Проведен  анализ  результатов  с  точки  зрения 
процессов локализации и делокализации носителей.

Kalit so'z
№ Havola nomi
1 [1] E. Dagotto. Rev. Mod. Phys. 66, 3, 763 (1994). [2] A.V. Puchov, P. Fournier, T. Timusk, N.N. Kolesnikov. Phys. Rev. Lett. 77, 9, 1853 (1996). [3] I.Ya. Fugol, V.N. Samovarov. FNT 22, 11, 1241 (1996). [4] D. Salamon, P. Abbamante, R. Liu, M. Klein, W. Lee, D. Gingsberg. Phys. Rev. B53, 2, 886 (1996). Fizikatverdogotela, 1997, tom 39, № 10 [5] V.M. Dmitriev, V.V. Yeremenko, I.S. Kachur, V.G. Piryatinskaya, O.R. Prixod'ko, A.M. Ratner, Ye.V. Xristenko, V.V. Shapiro. FNT. 21, 2, 219 (1995). [6] B. Moeckly, D. Lathrop, R. Buhrman. Phys. Rev. B47, 1, 400 (1993). [7] V.D. Okunev, N.N. Pafomov. Pis'ma v JTF 17, 9, 1 (1991). [8] E.I. Goldman, A.G. Jdan, V.N. Nemenushiy. FTP 12, 5, 833(1978). [9] W. Markowitsch, W. Mayr, P. Schwab, X. Wang. PhysicaC223, 1/2, 117 (1994). [ ]Z.Q. Qiu, Y.W. Du, H. Tang, J.C. Walker. J. Magn. Mater. 78, 359(1989). [ ]T. Tamaki, T. Komai, A. Ito, Y. Maeno, T. Fujita. Solid State Commun. 65, 43(1988). [ ]S. Suharan, J. Chadwick, D.B. Hannon, D.H.Janes,M.F. Thomas. Solid State Commun. 70, 817 (1989). [ ]M. Takano,Z. Hiroi, H. Mazaki,Y.Bando, Y.Takedo, R. Kanno. Physica C153/155, 860(1988). [ ]D. Hechel, I. Nowik, E.R. Bauminger, I. Felner. Phys.Rev.B42, 2166 (1990). [ ]V.F. Masterov, F.S. Nasredinov, Ch.S. Saidov, P.P. Seregin, S.I. Bondarevskiy, O.K. Sherbatyuk. SFXT 5, 1339 (1992). [ ]V.F. Masterov, F.S. Nasredinov, Ch.S. Saidov, P.P. Seregin, O.K. Sherbatyuk. FTT 34, 7, 2294 (1992). [ ]J.C. Love, F.E. Obenshain, G. Czjzek. Phys. Rev. B3, 2837 (1971).