EFFECTOFCOMPLEXING AGENT ON THE STRUCTURAL, OPTICALANDELECTRICALPROPERTIESOFPOLYCRYSTALLINEINDIUMSULFIDETHINFILMSDEPOSITEDBYCHEMICALBATHDEPOSITION

Admin bo'lib kirish (www.admin.slib.uz)

Tizim sinov (TEST) rejimida ishlamoqda! Murojat uchun @slib_support

Eski talqinga o'tish link

11 октябр 2024

Asosiy til:Ingliz

EFFECTOFCOMPLEXING AGENT ON THE STRUCTURAL, OPTICALANDELECTRICALPROPERTIESOFPOLYCRYSTALLINEINDIUMSULFIDETHINFILMSDEPOSITEDBYCHEMICALBATHDEPOSITION

Fan yo'nalishi:

67096b4c2208e.pdf

PDF

Eurasian Journal of Academic Research

Maqola chop etish see more

MAQOLA ANNOTATSIYASI

Indium sulfide (β-In2S3) thin films are synthesized by chemical bath deposition method using three different complexing agent volumes, triethanolamine (TEA) (0.30, 0.45, and 0.60 ml). The effect of complexing agent on the structural, morphological, optical and electrical properties of chemically deposited indium sulfide (β-In2S3) thin films have been investigated in this work. The characterization of the present films is carried out using X-ray diffraction, scanning electron microscopy, UV-vis spectroscopy and electrical measurements. The structure of the films is polycrystalline with a cubic phase of β-In2S3. Firstly, the band gap of the film decreases from 3.74 eV to 3.15 eV by adding 0.30 ml TEA. Then, it increases to 3.79 eV with increasing TEA. Nevertheless, previously, the refractive index of the films increases from 2.13 to 2.67 for the 0.30 mL TEA and then it decreases to the value of 2.11 with increasing TEA. Extinction coefficient, real and dielectric constant of the films are calculated using the absorption and transmittance spectra. Firstly, the electrical resistivity of the films decreases from 3.46 108 Ω cm to 1.33 107 Ω cm by adding 0.30 ml TEA. Then, it increases to the value of 2.16 109 Ω cm with increasing TEA. Eventually, the more conductive film with worm-like morphology detected from the scanning electron microscopy is synthesized using 0.30 ml TEA. These results show that complexing agent has an important effect on the structural, morphological, optical and electrical properties of the deposited films

MUALIFLAR

Teglar

# structural# morphological# optical and electrical# chemically# polycrystalline# decreases

Maqolani baholang

0

0 ta

Maqola idintifikatorlari

ROI:

https://eroi.uz/11.0201/A1024-0353

DOI:

Mavjud emas

Foydalanilgan adabiyotlar

[1]M.A.Mughal,R.Engelken,R.Sharma,Sol.Energy120,131(2015).[2]N.Khooshsirat,N.A.MdYunus,J.Electron.Mater.45,5721(2016).[3]ZhaoYangZhong,EouSikCho,SangJikKwon,ThinSolidFilms547,22(2013).[4]X.Zhang,C.Shao,X.Li,N.Lu,K.Wang,F.Miao,Y.Liu,J.Hazard.Mater.283,599(2015).[5]M.Pomaska,R.Sáez-Araoz,A.Steigert,Y.P.Fu, F. Hergert, I. Lauermann, Th. Dittrich, M.Ch. Lux-Steiner, Ch.-H. Fischer,Sol. Energy Mater. Sol. Cells132,303(2015).[6]S.S.Wang, F.J.Shiou, C.C.Tsao, S.W.Huang, C.Y. Hsu,Mater. Sci. Semicond. Proc.16, 1879(2013).[7]T. Sall, B.M. Soucase, M. Mollar, B. Hartitti, M. Fa-houme,J.Phys.Chem.Solids76,100(2015).[8]W.Xiang,H.Zhao,J.Zhong,H.Luo,X.Zhao, Z. Chen, X. Liang, X. Yang,J.AlloysComp.553,135(2013).[9]X.Meng,Y.Lu,X.Zhang,B.Yang,G.Yi,J.Jia, Appl.Surf.Sci.258,649(2011).[10]S.Kirtay,ActaPhys.Pol.A128,B-90(2015).[11]İ.Karahan,ActaPhys.Pol.A128,B-432(2015).[12]N.ÇiçekBezir,A.Evcin,R.Kayali,M.KaşikçiÖzen, K.Esen,E.B.Cambaz,ActaPhys.Pol.A130,300(2016)).[13]I.N. Qureshi, M.Shahid, A.N. Khan, ActaPhys.Pol.A128,B-314(2015).[14]W. Laslounia, M. Azzaz,ActaPhys.Pol.A130, 112(2016).[15]Y.SiAhmed, T.Hadjersi,R. Chaoui, ActaPhys.Pol.A130,385(2016).[16]M.Amlouk,M.A.BenSaid,N.Kamoun,S.Belgacem, N.Brunet,D.Barjon,Jpn.J.Appl.Phys.38,26(1999).[17]N.F.Mott,E.A.Davis,ElectronicProcessinNon-CrystallineMaterials,Clarendon,Oxford1979.[18]OpticalPropertiesofSolids,Ed.F.Abeles,North-Holland,London1972.[19]A.Timoumi,H.Bouzouita,Int.J.Renew.EnergyTechnol.Res.2,188(2013).[20]T.T.John,C.S.Kartha,K.P.Vijayakumar,T.Abe, Y.Kashiwaba,Vacuum80,870(2006).[21]P.M.R.Kumar,T.T.John,C.S.Kartha,K.P.Vi-jayakumar, T. Abe, Y. Kashiwaba, J. Mater. Sci.41,5519(2006).[22]P.Rao,S.Kumar,ThinSolidFilms524,93(2012).