Corrosion of metals, including steel, is a serious problem in many areas around the world. As a result of corrosion, the natural state of the materials is lost and the equipment is damaged. Therefore, the development of inhibitory compositions is of great theoretical and practical importance. Inhibitors react with metal surfaces or corrosive media, and form a protective coating on the metal surface. These coatings can consist of a metal oxide, an anode coating, a thin layer, a complex with a metal ion, or an adsorption ion coating. One way to protect metals from corrosion is to use organic inhibitors that contain heterocyclic compounds that contain phosphorus, sulfur, and nitrogen

  • Ссылка в интернете
  • DOI
  • Дата создание в систему UzSCI 24-11-2022
  • Количество прочтений 149
  • Дата публикации 12-11-2020
  • Язык статьиIngliz
  • Страницы52-57
English

Corrosion of metals, including steel, is a serious problem in many areas around the world. As a result of corrosion, the natural state of the materials is lost and the equipment is damaged. Therefore, the development of inhibitory compositions is of great theoretical and practical importance. Inhibitors react with metal surfaces or corrosive media, and form a protective coating on the metal surface. These coatings can consist of a metal oxide, an anode coating, a thin layer, a complex with a metal ion, or an adsorption ion coating. One way to protect metals from corrosion is to use organic inhibitors that contain heterocyclic compounds that contain phosphorus, sulfur, and nitrogen

Русский

Коррозия металлов, включая сталь, является серьезной проблемой во многих регионах мира. В результате коррозии естественное состояние материалов теряется, а оборудование повреждается. Поэтому разработка ингибирующих композиций имеет большое теоретишеское и практическое знашение. Ингибиторы реагируют с металлическими поверхностями или агрессивными средами и образуют защитное покрытие на металлической поверхности. Эти покрытия могут состоять из оксида металла, анодного покрытия, тонкого слоя, комплекса с ионом металла или адсорбчионного ионного покрытия. Одним из способов защиты металлов от коррозии является использование органических ингибиторов, которые содержат гетерочиклические соединения, которые содержат фосфор, серу и азот

Ўзбек

Дунё бўйлаб металларнинг, шу жумладан пўлатнинг коррозияси жиддий муаммодир. Коррозия натижасида материалларнинг табиий холати йўқолади ва ускуналар бузилади. Шунинг ушун инхибитив композицияларнинг ривожланиши катта назарий ва амалий ахамиятга эга. Инхибиторлар металл юзалар ёки коррозий мухит билан реакцияга киришади ва металл юзасида химоя қопламини хосил қилади. Ушбу қопламалар металл оксиди, анод қопламаси, юпқа қатлам, металл иони билан комплекс ёки адсорбчион ион қопламасидан иборат бўлиши мумкин. Металлларни коррозиядан химоя қилишнинг бир усули - бу фосфор, олтингугурт ва азотни ўз ичига олган цетеросиклик бирикмаларни ўз ичига олган органик инхибиторлардан фойдаланиш.

№ Название ссылки
1 Андреев‖ И.Н.‖ Введение‖ в‖ коррозиологию:‖ Ушебное‖ пособие.‖ Казан:‖ Изд-во‖ Казанского‖государственного‖технологишеского‖ун-та,‖2004.‖-140‖с
2 Новый‖ справошник‖ химика‖ и‖ технолога.‖ Электродные‖ прочессы.‖ Химишеская‖ кинетика‖ и‖ диффузия.‖ Коллоидная‖ химия.‖ Под‖ ред.‖ Акад.‖ Раен,‖ д.х.н.,‖ проф.‖ Симановой‖С.А.‖Санкт-Петербург,‖НПО‖Профессионал,‖2006.‖
3 Xiao F, Qian C, Guo M, et al. Anticorrosive durability of zinc based waterborne coatings enhanced by highly dispersed and con ductive polyaniline/graphene oxide composite. Prog Org Coat. 2018;125:79–88
4 Tenga S, Gaob Y, Cao F, et al. Zinc-reduced graphene oxide for enhanced corrosion protection of zinc-rich epoxy coatings. Prog Org Coat. 2018;123:185–189
5 Mohammadi S, Roohi H. Influence of functionalized multi-layer graphene on adhesion improvement and corrosion resistance per formance of zinc-rich epoxy primer. Corros Eng Sci Techn. 2018;53(6):422–430.
6 Wang X, Liu X, Yuan H, et al. Noncovalently functionalized gra phene strengthened poly (vinyl alcohol). Mater Des. 2018;139:372–379.
7 Fahim I, Tridane M, Belaaouada S. Physico-chemical‖ studies‖ of‖ MgNa3P3O10·12‖ H2O. MATEC Web Conf. 2013;5:04035. doi:10. 1051/matecconf/20130504035.
8 Hayatdavoudi H, Rahsepar M. Smart inhibition action of layered double hydroxide nano containers in zinc-rich epoxy coating for active corrosion protection of carbon steel substrate. J Alloy Compd. 2017;711:560–567.
9 Андреев‖ И.Н.‖ Введение‖ в‖ коррозиологию:‖ Ушебное‖ пособие.‖ Казан:‖ Изд-во‖ Казанского‖государственного‖технологишеского‖ун-та,‖2004.‖-140‖с
10 ‖Под‖ ред.‖Акад.‖ Раен,‖ д.х.н.,‖ проф.‖ Симановой‖ С.А.‖ ‖Новый‖ справошник‖ химика‖ и‖ технолога.‖ Электродные‖ прочессы.‖ Химишеская‖ кинетика‖ и‖ диффузия.‖ Коллоидная‖ химия.‖Санкт-Петербург,‖НПО‖Профессионал,‖2006
11 Beknazarov, K.S., Dzhalilov, A.T., Ostanov, U.Y., Erkaev, A.M. The inhibition of the corrosion of carbon steel by oligomeric corrosion inhibitors in different media. International Polymer Science and Technology 2015.
12 . Дятлова Н.М., Темкина В.Я., Попов К.И.. Комплексоны‖и‖комплексонаты‖металлов‖ - М.:‖Химия,‖1988.‖- 544‖с.‖Режим‖ доступу‖- http://chemteq.ru/library/inorganic/2022.html2.
13 Alsabagh, A.M., M.A. Migahed, and H.S. Awad, Reactivity of polyester aliphatic amine surfactants as corrosion inhibitors for carbon steel in formation water (deep well water). Corrosion Science, 2006. 48(4): p. 813-828.
14 Fares, M.M., A.K. Maayta, and M.M. Al-Qudah, Pectin as promising green corrosion inhibitor of aluminum in hydrochloric acid solution. Corrosion Science, 2012. 60: p. 112-117
15 . Narzullaev A.X., Beknazarov H.S., Jalilov A.T., Rajabova M. F. Studying the Efficiency of Corrosion Inhibitor Iktsf-1, Ir-Dea, Ir-Dar-20 in 1m Hcl International Journal of Advanced Science and Technology Vol. 28, No. 15, (2019), pp. 113-122
16 Narzullaev A.X., Djalilov A.T., Beknazarov X.S. Evaluation of inhibiting properties of IC-DALR-1 corrosion inhibitor in aqueous and saline media. Austrian Journal of Technical and‖Natural‖Sciences‖№‖5–6 2019 May– June
17 A.S. Yaro, N.Sh. Abdul Masih, A.A. Khadom, The influence of temperature on corrosion inhibition of carbon steel in airsaturated 7N H3PO4 by potassium iodide, Iraqi J. Chem. Petrol. Eng. 1 (2000) 83–87.
18 A.Y. El-Etre, M. Abdallah, Z.E. El-Tantawy, Corrosion inhibition of some metals using lawsonia extract, Corros. Sci. 47 (2005) 385–395.
19 A.A. Khadom, A.S. Yaro, A.S. AlTaie, A.A.H. Kadum, Electrochemical, activations and adsorption studies for the corrosion inhibition of low carbon steel in acidic media, Portug. Electrochim. Acta 27 (6) (2009) 699–712
20 A.Y. Musa, A.A. Khadom, Abdul Amir H. Kadhum, Abu Bakar Mohamad, Mohd Sobri Takriff, Kinetic behavior of mild steel corrosion inhibition by 4-amino-5-phenyl-4H-1,2,4- trizole-3-thiol, J. Taiwan Inst. Chem. Eng. 41 (2010) 126–128
В ожидании