STUDYING OF THE MATERIAL COMPOSITION AND DEVELOPMENT OF THE TECHNOLOGY OF PROCESSING OF GOLD-CONTAINING SULFIDE SAMPLES OF ONE OF THE DEPOSITS OF THE REPUBLIC UZBEKISTAN

Maqolada oltin sulfidli ma'danli namunalarni qayta ishlash texnologiyasi va moddiy tarkibini 
o'rganish natijalari bayon etilgan. Javhar namunalarining moddiy tarkiblari oltin va kumushdan 
spektral, kimyoviy, tahlil va oqilona tahlillar orqali o'rganiladi. Rudalar namunalarining moddiy 
tarkibini o'rganish asosida quyidagi xulosalar berildi: oltin va kumush sanoatning eng qimmatli 
qismlari.  Graviyofloraf  kontsentrati  kubiklaridan  sulfat  kislota  bilan  ishlashni  qo'llash 
jarayonning  texnologik  samaradorligini  oshirish imkonini  beradi.  Gravio-flotatsion  konsentrat 
aralashmasini  sulfat  kislota  bilan  ishlov  berilgandan  keyin  95%  CL  kattalikda  maydalash 
natijasida.  -0,074+0  va  sorpsion  sianlash  olib  boriladi.  Dastlabki  tortishda  tarkibida  oltin  -77.83  va  kumush  -16.3,  natriy  sianid  konsentratsiyasi  0,15%,  nisbati  q:s=2:1;  AM-2B-5%, 
sianlash  muddati  36  soat.oltin  -  6.5,  kumush  esa  4.8   eritmada  va  smolada  asil  metallarning 
olinishi  kuyidagi  tarkiblar  mos  ravishda  91.65  va  70.55%  ni  tashkil  etgan.  Rudadan  87.63% 
oltin va 55.6% kumush qazib olinadi.

The  article  discusses  the  results  of  studying  the  material  composition  and  the 
development  of  technology  for  processing  gold-bearing  sulfide  ore  samples.  The  material 
composition of the ore samples was studied by spectral, chemical, assay and rational analysis of 
gold and silver. Based on a study of the material composition of the ore samples, the following 
Chemistry   and   chemical   technology
70
conclusions were made: gold and silver are the industry's most valuable components. It is shown 
that  the  use  of  sulfuric  acid  treatment  of  a  cinder  of  graviofloraf  concentrate  can  allow  to 
improve  the  technological  performance  of  the  process.  As  a  result  of  the  mixture  of  gravio flotation  concentrate  after  sulfuric  acid  treatment  drying,  grinding  to  a  size  of  95%  CL.  -0,074+0 mm and subjected to sorption cyanidation. In the initial cake, the content of gold -77.83 
u. e. and silver-16.3 u. e., the concentration of sodium cyanide 0.15%, the ratio W:t=2:1; resin 
AM-2B-5% of the pulp volume, the duration of cyanidation 36 hours.the Content in the tailings 
of cyanidation of gold  -  6.5 u. e., and silver  -  4.8 u. e. the Extraction of noble metals in solution 
and on the resin was 91.65 and 70.55%, respectively. Through extraction of 87.63% gold and 
55.6% silver from ore.

В  статье  рассматриваются  результаты  изучения  вещественного  состава  и 
разработка  технологии  переработки  золотосодержащих  сульфидных  проб  руды. 
Вещественный  состав  проб  руды  изучен  спектральным,  химическим,  пробирным  и 
рациональным  анализами  на  золото  и  серебро.  На  основании  изучения  вещественного 
состава  проб  руды  сделаны   следующие  выводы:  промышленно-ценными  компонентами 
пробы являются золото и серебро. Показано, что применение сернокислотной обработки 
огарка  гравио-флотоконцентрата  может  улучшить  технологические  показатели 
процесса.  В  результате  смеси  гравио-флотоконцентрата  после  сернокислотной 
обработки  сушки,   измельчении  до  крупности  95%  кл.  -0,074+0  мм  подвергали 
сорбционному цианированию. В исходном кеке содержание золота  -77,83 у. е. и серебра  -16,3 у. е., концентрация цианистого натрия 0,15%, соотношение ж:т=2:1; смола АМ-2Б-5%  от  объема  пульпы,  продолжительность  цианирования  36  ч.  Содержание  в  хвостах 
цианирования золота  -  6,5 у. е., и серебра  -  4,8 у. е. Извлечение благородных металлов в 
растворе   и  на  смолу  составило  91,65  и  70,55%,  соответственно.  Сквозное  извлечение
золота -87,63% и серебра - 55,6% из руды.