PLASTIFITSIRLANGAN GIPS OLISHDA FENOL FORMALDEGID ASOSIDAGI KREMNIYORGANIK POLIMERDAN FOYDALANISH

This article highlights the possibilities of obtaining plasticized gypsum with compositions based on phenol-formaldehydetriethoxysilane. We also studied the physical and mechanical properties of samples obtained with a gypsum mixture containing various concentrations of polymer compositions, such as water permeability, flexural and compressive strength, including a decrease in water permeability up to 50-60%, an increase in flexural strength up to 20-56% was determined, for compression up to 20-47%.

Ushbu makolada fenolformaldegidotrietoksisilan asosida yaratilgan kompozitsiyalar orqali plastifikatsialangan gips olish imkoniyatlari yoritilgan. Shuningdek, tarkibida turli xil konsentratsiyali polimer kompozitsiyalari saglagan gpis qorishmasi orqaali olingan namunalarning suv shimuvchanligi, egilish va siqilishdagi mustahkamligi kabi fizik-mexanik xossalari o‘rganilgan, jumladan, suv shimuvchanliknin 50-60% gacha kamayishi, 20-56 % gacha egilishdagi, 20-47 % gacha siqilishdagi mustahkamligining oshishi aniqlangan.

В данной статье освещены возможности получения пластифицированного гипса композициями на основе фенолформальдегидтриэтоксисилана. Также были изучены физико-механические свойства образцов, полученных гипсовой смесью, содержащей различные концентрации полимерных композиций, такие как водопроницаемость, прочность на изгиб и сжатие, в том числе снижение водопроницаемости до 50-60%, определено увеличение прочности на изгиб до 20-56%, на сжатие до 20-47%.